Epoxy Resins
Cold to Hot Curing: Wet-Layup
| Resin | Hardener | Mixing Ratio (% Weight) | Pot Life Min 25°C | Curing Temp. | Post Curing | Tg °C Max | Applications / Properties |
|---|---|---|---|---|---|---|---|
| EC 130LV Light violet | W 341 Neutral | 100:30 | 8 - 15 min. (100 ml) | Room tem. / 70 °C | (120 °C) | 125 | Short, medium, long, extra long pot-life, thermal resistant, high performance system. W 342 UV resistant. W 132, W 152 XLR, W340 are recommended for medium and large surface vacuum bag laminatig. |
| EC 130LV Light violet | W 342 Neutral | 100:30 | 22 - 27 min. (100 ml) |
Room tem. / 70 °C | (120 °C) | 118 | |
| EC 130LV Light violet | W 340 Neutral | 100:30 | 50 - 70 min. (100 ml) |
Room tem. / 70 °C | (120 °C) | 135 | |
| EC 130LV Light violet | W 152 XLR Neutral | 100:30 | 180 - 200 min. (100 ml) |
Room tem. / 70 °C | ( 80 °C) | 103 | |
| EC 130LV Light violet | W 132 Neutral | 100:38 | 240 - 280 min. (100 ml) |
Room tem. / 70 °C | ( 80 °C) | 100 | |
| EC 152 | AW 90 AW 91 AW 92 | 100:50 | 10-14 min 35-45 min 65-80 min | Room tem. / 70 °C | ( 70 °C) | 75 85 82 | Coupling layer between cured and wet lay-up laminating (also on vinylester cured layer) . |
| EC 152 Neutral |
W 152 HR Neutral | 100:30 | 12 - 17 min. (200 ml) |
Room tem. / 70 °C | ( 70 °C) | 80 | High performance resin with short, medium, long, extra long pot-life hardeners, for: - small pieces wet-lay-up laminating at R.T - medium and large surface vacuum bag laminating |
| EC 152 Neutral |
W 152 MR Neutral | 100:30 | 35 - 45 min. (200 ml) |
Room tem. / 70 °C | ( 70 °C) | 107 | |
| EC 152 Neutral |
W 152 LR Neutral | 100:30 | 90 - 110 min. (200 ml) |
Room tem. / 70 °C | ( 70 °C) | 104 | |
| EC 152 Neutral |
W 152 XLR Neutral | 100:30 | 100 - 120 min. (200 ml) |
Room tem. / 70 °C | ( 70 °C) | 97 | |
| EC 255 Neutral | W 152 HR W 152 XLR | 100:24 | 14 - 20 min. 125 - 160 min. | Room temperature | ( 70 °C) | 67 77 | Thixotropic resin, fast or extra long gelification, for bonding PVC foam core in sandwich laminating structures. |
| EC 155 | W 155 Neutral | 100:35 | 9 - 13 min. (100 ml) | Room tem. / 50 °C | ( 60 °C) | 87 | Resin with very fast reaction hardeners for large scale sport items production. W155 for laminating parts; W558 as binder for putty. |
| Neutral | W 558 Neutral | 100:35 For putty add: -EF18T or -EF 23 or -EF 232 | 7 - 10 min. (100 ml) | Room temperature | ( 60 °C) | 85 |
Cold to Hot Curing: Press Moulding - RTM
| EC 14 | W 340 | 100:27 | 80 - 100 min. (8 min. 80°C) | Room tem. / 100 °C | (100-130 °C) | 150 | Room temperature long pot-life system with high reactivity in hot press moulding (ex. for wakeboards, snowboards, etc.). |
| EC 577 Neutral | K 12 | 100:25 | 20 - 30 min. (100 ml) | 50 - 70°C | (70 °C) | 85 | Fast curing systems for high temperature RTM process). |
| W 342 Neutral | 100:30 | 15 - 25 min. (100 ml) |
60 °C | (120 °C) | 120 | ||
| EC 131LV Light violet | W 342 Neutral | 100:25 | 22 - 32 min. (100 ml) | Room tem. / 50 °C | (120 °C) | 92 | |
| EC 157 Neutral | W 557 Neutral | 100:18 | 20 - 30 min. (100 ml) | Room tem. / 100 °C | (120 °C) | 100 |
Cold Curing + Post Curing: Infusion
| EC 157 Neutral | W 152 MR | 40 - 50 min. (200 ml) | 102 | Very low viscosity and medium - long pot-life system. Suitable for medium and large infusion component (i.e. wind turbine blades and boats). | |||
| W 152 MLR Neutral | 100:30 | 80 - 100 min. (200 ml) |
Room tem. / 50 °C | ( 70 °C) | 90 | ||
| W 152 XLR Neutral | 120 - 150 min. (100 ml) |
90 |
2-Component Systems - Cold or Moderate Temperature Curing
 | Aspect | Mixing Ratio bu Weight Mix Ratio by Volume | Pot Life (100ml, RT) minutes | Recommended Curing Cycle. | Tg °C Max | Shear Strength (N/mm2) | Applications / Properties | |
|---|---|---|---|---|---|---|---|---|
| E P O X Y |
AS52/AW11 (ADH52.11) |
Fluid Transparent Lightly yellow |
100:100 100:100 | 3-4 | 2h 25 °C or more | 45 | 11-13 Alum 11-13 Inox | Aluminium, steel, plastic, composite fast repairing and bonding. AS88 is recommended for bonding vertical surfaces. |
| AS44/AW09 | Lightly thixo Amber |
100:80 100:100 | 40-50 | 7 days at RT or 6 h at 60÷80 °C |
70 | 21-26 Alum 21-26 Inox | Universal adhesives with different viscosity. Aluminium, steel, carbon composite and FRP part, wood, glass, ceramic, plastic and machinable board structural bonding. | |
| AS90/AW42 (ADH90.42) |
Heavy thixo Milky |
100:80 100:100 | 30-45 | 7 days at RT or 6 h at 60÷80 °C |
70 | 30-37 Alum 17-21 Inox | ||
| AS89/AW89 and new AS89.1/AW89.1 (ADH89.89) |
Thixotropic Black Contrasting colours |
100:45 100:50 | 20-30 | 2h at 80 °C or 5h at 50 °C |
90 | 27-33 Alum 27-33 Inox 32-39 Carbon fiber laminated | Composite part fatigue resistant structural bonding (car, bike, sporting goods) and different nature material bonding (aluminium, steel, FRP, glass, ceramic). High thermal and chemical resistance. | |
| AS90/AW90 (ADH90.90) |
Heavy thixotropic Lightly contrasting colours No sag till 10 mm |
100:45 100:50 | 10-15 | 7 days at RT or 5h at 70 °C | 75 | 25-30 Alum 26-31 Inox | Wind turbine blade, aircraft, boat hull, train part fatigue resistant structural bonding and different nature material bonding (aluminium/ FRP/ honeycomb/ steel/ ceramic/ glass). High chemical resistance. | |
| AS90/AW91 (ADH90.91) |
35-45 | 80 | ||||||
| AS90/AW92 | 65-80 | 80 | ||||||
| AS7/AW6 | Filled Heavy thixo Beige |
100:100 100:100 | 25-35(**) | 3-7 days at RT | 60 | 11-15 Alum 16-20 Inox | Natural stone structural bonding and different nature material bonding. Smoothing, sealing and fastening in civil engineering. | |
| AS7/AW8 | 10-16(**) | 7-9 Alum 16-18 Inox | ||||||
| AS15/AW15+ EF18T | Thixotropic Milky filled with EF 18T green |
100:15:20 | 10-18 | 24h at RT or 2h at 70-75 °C | 103 | 8-10 Alum | Thixotropic adhesive with separated filler for epoxy board bonding and putty | |
| AS50/AW50 (ADH50.50) |
Filled Heavy thixo Dark grey Contrasting colours |
100:50 100:50 | 15-25(**) | 7 days at RT or 6h at 60÷80 °C | 105 | 14-18 Alum 18-22 Inox | Pultruded part, SMC, ferrite, metal, ceramic and glass structural bonding. Low thermal expansion coefficient, good thermal conductivity. High chemical and thermal resistance. AS60/AW60 can work up to 150°C. | |
| AS60/AW60 | Filled Heavy thixo Dark grey Contrasting colours |
100:50 100:50 | 25-35(**) | 15h at RT or 3h at 130-150 °C | 135 | 14-18 Alum 15-19 Inox | ||
| P U |
PC36L/G30 | Filled PU Thixotropic Neutral milky |
100:25 100:30 | 4-8 | 1-2 days at RT | 45 | 7-9 Alum 4-5 PMMA | Termoplastic, FRP and polyurethane machinable boards semirigid bonding. |
| ADH PU 3005 flexible translucent | Unfilled PU very tixotropic |
100:100 | 4-6 | 8h at RT | -10 50 55 |
6-8 PVC 6-8 PA 10-12 Alum 7-8 ABS 8-10 SMC 11-14 Alu 10-12 Inox 13-15 FRP |
Three type of sealant adhesives PU, flexible ShoreA85, low module Shore D60, rigid Shore D85 for fast repairing and bonding thermoplastic, FRP and many other materials (available in cartridge with static mixer and manual dispenser for 50 ml, 200 ml, 400 ml). | |
| ADH PU 6005 low module translucent | ||||||||
| ADH PU 8505 rigid black | ||||||||
(*) Suggested curing cycle is recommended in order to achieve the best properties. For other curing cycles refer to data sheets, (**) Pot-life 200ml, RT
1-Component Systems - Hot Curing
| E P O X Y |
ASM 030 (ADHH030) |
Thixotropic Milky No sag at high T |
1-COMP | 4 month 25 °C or 12 month 0 °C | 2h at 120 °C | 135 | 14-16 Alum 17-20 Inox | Metal, ceramic, ferrite and composite structural bonding high thermal resistant. |
|---|---|---|---|---|---|---|---|---|
| ASM 101 | Filled Heavy thixio Blue |
1-COMP | 4 month 25 °C or 12 month 0 °C | 2h at 120 °C | 100 | 20-23 Inox | One-component lamellar abrasive disk manufacturing. |